Title: | Alkali treatment for single-stage co-evaporated thin CuIn0.7Ga0.3Se2 solar cells | Authors: | DE WILD, Jessica Simor, Marcel BULDU KOHL, Dilara KOHL, Thierry BRAMMERTZ, Guy MEURIS, Marc POORTMANS, Jef VERMANG, Bart |
Issue Date: | 2019 | Source: | THIN SOLID FILMS, 671, p. 44-48 | Abstract: | KF and NaF treatments were done for single-stage co-evaporated CuIn0.7Ga0.3Se2. The absorber layers were grown on a substrate with an alkali barrier layer and NaF was either added before or after absorber layer growth. No differences were found on the device performance amongst the procedures to add Na. This is expected if the single-stage process does not have a copper rich stage or a Ga gradient, which is likely since there was no change of the elemental fluxes during absorber layer growth and no Ga profile was measured. KF was added by post-deposition only. Current-voltage characteristics were measured and net doping concentrations were determined from capacitance-voltage measurements (CV). We see an improvement of the open-circuit voltage (Voc) with increasing KF amount, and a marginal increase of the fill factor. CV measurements showed increasing net acceptor concentration with increasing KF amount. Time resolved photoluminescence (PL) showed an increased decay time for KF treated cells and the PL peak shape changed. Without KF treatment the PL peak is symmetric, after KF treatment a further peak appears at higher energy in the PL spectrum. This higher energy peak increases in intensity with increasing KF concentration. The same effects were seen in a sample without Na, but here the Voc was limited due to large tailing. Hence both Na and K are required for good cell efficiencies. | Keywords: | Copper indium gallium selenide; Solar cells; Single-stage; Alkali treatment; Thin film; Co-evaporation | Document URI: | http://hdl.handle.net/1942/28445 | ISSN: | 0040-6090 | e-ISSN: | 1879-2731 | DOI: | 10.1016/j.tsf.2018.12.022 | ISI #: | 000455998000008 | Category: | A1 | Type: | Journal Contribution | Validations: | ecoom 2020 |
Appears in Collections: | Research publications |
Files in This Item:
File | Description | Size | Format | |
---|---|---|---|---|
DeWild2018_AlkaliTreatment_TSF-D-18-00933R2.pdf | Peer-reviewed author version | 1.18 MB | Adobe PDF | View/Open |
1-s2.0-S0040609018308319-main.pdf Restricted Access | Published version | 828.08 kB | Adobe PDF | View/Open Request a copy |
SCOPUSTM
Citations
4
checked on Sep 5, 2020
WEB OF SCIENCETM
Citations
11
checked on Oct 15, 2024
Page view(s)
236
checked on Jul 31, 2022
Download(s)
178
checked on Jul 31, 2022
Google ScholarTM
Check
Altmetric
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.